Pump Packings
|
|
ICP 261Braided packing manufactued from cotton yarns added with tallow lubricant (both outside and inside).
|
|
|
ICP 906Braided packing manufactured from high quality flax yarns added with PTFE dispersion and running-in lubricant.
|
|
|
ICP 907Braided packing manufactured from acrylic fibre yarn added with special PTFE lubricant, silicone free.
|
|
|
ICP 907GBraided packing manufactured from acrylic fibre yarn added with high performance lubricant and graphite powder.
|
|
|
ICP 907RBraided packing manufactured from pure ramie yarn added with special PTFE lubricant, silicone free.
|
|
|
ICP 908Braided packing manufactured from high quality phenolic “Kynol ฎ ” fiber yarn added with PTFE dispersion and running-in lubricant.
|
|
|
ICP 909Braided packing manufactured from PTFE filaments added with running-in lubricant.
|
|
|
ICP 910Braided packing manufactured from PTFE filaments added with PTFE dispersion.
|
|
|
ICP 910MBraided packing manufactured from PTFE filaments added with PTFE dispersion and central core of temperature resistant elastomer.
|
|
|
ICP 912Braided packing manufactured from high quality carbon fiber yarn with PTFE and graphite lubricant.
|
|
|
ICP 913Braided packing manufactured from high quality carbon fiber yarn with Inconel wire and running-in graphite lubricant.
|
|
|
ICP 914Braided hybrid packing manufactured from combination of PTFE fiber yarn and “Twaron” aramid fiber yarn in the corner.
|
|
|
ICP 914TBraided hybrid packing manufactured from combination of GFOฎ fiber yarn and “Twaron” aramid fiber yarn in the corner added with PTFE dispersion outside.
|
|
|
ICP 915Braided hybrid packing manufactured from a combination of PTFE fiber yarn added with special lubricant and “Twaron” aramid fiber yarn in the corners.
|
|
|
ICP 915S
|
|
|
ICP 916Braided packing manufactured from expanded PTFE yarn containing graphite and silicone oil as lubricant. 100% GOREฎ GFOฎ Fiber.
|
|
|
ICP 917Braided packing manufactured from high strength continuous “Twaron” para-aramid yarns added with PTFE dispersion and inert lubricant.
|
|
|
ICP 922Braided packing manufactured from PTFE filaments added with non-lubricated graphite.
|
|
|
ICP 923Braided packing manufactured from high strength discontinuous “Kevlar” para-aramid yarns added with PTFE dispersion and inert lubricant.
|
|
|
ICP 924Braided hybric packing manufactured from combination of GFOฎ fiber yarn with “Kevlar” fiber yarn inside.
|
|
|
ICP 925Braided packing manufactured from high quality expanded graphite ribbons with a low chloride content, treated with special corrosion inhibitors.
|
|
|
ICP 925CBraided hybrid packing manufactured from high purity expanded graphite ribbons combined with high quality carbon fiber yarns in the corners.
|
|
|
ICP 925TeBraided packing manufactured from graphite fiber yarn blended with PTFE lubricant.
|
|
|
ICP 926Braided packing manufactured from high strength discontinuous para-aramid yarns added with PTFE dispersion, graphite powder and inert lubricant.
|
|
|
ICP 931Braided packing manufactured from ePTFE yarn with high lubricant content for superior heat dissipation.
|
|
|
ICP 936Braided packing manufactured from PTFE filaments added with high quality graphite based lubricant.
|
|
|
ICP 936G
|
|
|
ICP 940B
|